Magnesia calcined from magnesite as raw material, superfine magnesium hydroxide has been produced by hydration.

以菱镁矿煅烧所得氧化镁为原料, 水化制备超细氢氧化镁.

互联网摘选

Aswell known , the main material of cathode carbon used in aluminium industry is calcined anthracite.

在铝用阴极碳块生产中,其主要原料为电煅烧无烟煤.

网络文摘精选

The results show that single-phase CZP powder is synthesized at 700 ℃ by the chelate-sol-gel method, which shows good sintering activity at a low temperature;

结果表明：络合溶胶-凝胶法合成的前驱物经700℃煅烧能得到单相CZP粉体，该粉体具有良好的低温烧结活性。

互联网摘选

Using burnability index to control the burning temperature of rotary kiln

用生料易烧性指数控制回转窑煅烧温度

互联网摘选

Studies on the mechanism of leaching silicon and aluminum from bentonite have been processed by adjusting reaction time, calcination temperature, ratio of alkali to bentonite, the kind of alkali etc.

并通过改变反应时间、煅烧温度、碱土比、碱的种类、以及焙烧与否，对膨润土的硅、铝浸出机理作了比较深入的研究。

互联网摘选

Application of pulse combustion technology covers heating boiler, chemical decomposition and synthesis, calcinations of lime and cement.

脉动燃烧技术的应用范围涉及锅炉采暖、化工分解与合成、石灰水泥煅烧等工业生产。

互联网摘选

Metallurgy To heat ( ores ) in a furnace in order to dehydrate, purify, or oxidize before smelting.

煅烧 ( 矿石):为在熔化前脱去水份 、 提纯或氧化而在熔炉里焙烧(矿石 )

网络文摘精选

Dead-Burned Magnesite is produced with selected natural magnesite through purifying calcining in shaft kiln.

重烧镁砂是选用天然菱镁石矿,经高温竖窑煅烧而成的.

互联网摘选

The effects of loading, calcination temperature and calcination time on the solid base catalyst preparation conditions on the yield of dehydroacetic acid.

通过实验考察了负载量、煅烧温度和煅烧时间等固体碱催化剂制备条件对脱氢乙酸产率的影响。

互联网摘选

The change of SO2 partial pressure, O2 partial pressure, average porosity and average pore radius of product layer on unreacted core were discussed based on the model. The features of calcination in constant temperature were also discussed.

在本文所建立模型的基础上讨论了未反应核表面SO2、O2分压的变化，产物层平均孔径和平均孔隙率的变化，并且讨论了实验工况难以实现的恒温煅烧特性。

互联网摘选

Additionally, the factors such as the ultrasonic conditions, the use of absolute ethyl alcohol, the abstersion and desiccation of the separated precipitation and the conditions of calcinations, which have influence on the preparation of the tungsten trioxide nanoparticles, have been discussed also.

讨论了超声条件、无水乙醇的使用、沉淀的分离洗涤与干燥以及煅烧条件等因素对制备WO3纳米颗粒的影响。

互联网摘选

When produce dense sodium carbonate with the material of natural alkali, a plenty of alkaline scrap material or alkaline mud which can alkalify the earth, pollute the air and environment is manufactured, using the scrap material by calcine with a large movable kiln is expensive.

在以天然碱为原料生产重质纯碱时，伴生大量碱性废渣（俗称苛化泥），此废渣堆放或坑埋，碱化土壤，污染环境和空气，若用大型回转窑煅烧处理，成本高不经济。

互联网摘选

The colloid ed alumina hydroxide was prepared by precipitation using PEG as dispersing agent. Then the colloid was calcined at 800~ 1100 ℃/ 2h to get the nano powder of alumine.

以不同聚合度的聚乙二醇（PEG）为分散剂，采用沉淀法制备氢氧化铝胶体，胶体经800~1100℃高温煅烧得到纳米氧化铝粉体。

互联网摘选

In this paper, we discuss the hydration mechanism of anhydrite ⅱ, study accelerating actions anhydrite ⅱ with different accelerating agent, fabricate the white anhydrite cement adding burned alunite and assimilation lime as the accelerating agents.

在探讨AⅡ无水石膏水化机理的基础上，研究了不同激发剂对AⅡ无水石膏的激发作用，采用内掺煅烧明矾石和消石灰制成了硬石膏白水泥。

互联网摘选

Effect of calcined anhydrite on Portland cement

煅烧硬石膏对硅酸盐水泥水化过程的影响

互联网摘选

Through the examination of the sample's physical nature and hydration and the analysis of its hydration mechanism, it revealed that calcined phosphogypsum, slag, clinker, and chemical activators in a certain mixing ratio are ground finely to make the anhydrite cement with higher compression.

通过对样品的物理性能和水化产物的检测以及水化机理的分析表明：将高温煅烧磷石膏、矿渣、熟料和激发剂按一定的比例混合磨细可以制备出高强的硬石膏水泥。

互联网摘选

Zhenjiang Carbon Products Plant ( ZJCP ) founded in 1986, is specialized in producing petroleum coke.

镇江市 碳素制品厂始建于1986年, 是生产煅烧石油焦的专业厂家.

互联网摘选

The particles of the carbide slag were continuously attrited in the calcination/ carbonation cycles. The attrition rate of particles of the carbide slag decreases with the number of cycles.

电石渣颗粒在循环煅烧/碳酸化过程中不断磨损，磨损速率随循环次数增加逐渐降低。

互联网摘选

Under laboratory conditions, after calcined at the temperature of 700 ℃, red-mud is mixed with cement to produce a special kind of concrete, with which the standard concrete is compared in terms of breaking and stress intensity.

在实验室条件下，对赤泥进行700℃的煅烧处理，并利用其制取水泥赤泥混凝土，与基准混凝土的抗折、抗压强度进行对比。

互联网摘选

Pure β-Ca 2P 2O 7 phase, pure β-tricalcium phosphate phase and hydroxyapatite containing a small amount of CaO were obtained by calcining the dried gel-like powders with the corresponding Ca/ P ratios at 1000 ℃.

将混合溶液蒸发溶剂后得到的干胶状粉末在1000℃煅烧，对应不同的Ca／P比，可分别获得纯β－Ca2P2O7和β－磷酸三钙以及含有极小量CaO的羟基磷灰石。

互联网摘选